GENERAL DESCRIPTION
PLIOGRIP EPOXY RESIN PER 205 is an unmodified liquid epoxy resin of medium viscosity that can be used with an aliphatic amine hardener PH 105 for hand lay-up applications. PLIOGRIP PH 105 is a low viscosity room temperature curing liquid hardener. This system gives a short pot life and fast cured at normal ambient temperatures. Products made from this system can be subjected to working temperature of 100°C.
TYPICAL PROPERTIES OF PLIOGRIP EPOXY RESIN PER 205
|
Properties |
Values |
|
Type |
Unmodified viscous epoxy resin |
|
Specific gravity @ 25°C |
1.14 -1.20 |
|
Appearance |
Clear to pale yellow liquid |
|
Epoxy equivalent |
180 - 200 |
|
Viscosity @ 25°C (CPS) |
9000 - 13000 |
|
Chlorine content (max.%) |
0.2 |
TYPICAL PROPERTIES OF PLIOGRIP HARDENER PH 105
|
Properties |
Values |
|
Type |
Aliphatic Amine |
|
Specific gravity @ 25°C |
0.95 -1.05 |
|
Appearance |
Pale yellow liquid |
|
Viscosity @ 25°C (CPS) |
20 - 30 |
MIX RATIO (PARTS BY WEIGHT) AND POT LIFE AT 25°C IN MINUTES
|
PLIOGRIP EPOXY RESIN PER 205 |
PLIOGRIP HARDENER PH 105 |
POT LIFE |
|
100 |
10 - 12 |
45 |
|
|
||
CURING TIME:
|
Curing temperature °c |
30 |
40 |
80 |
100 |
|
Curing time |
14-24 hrs |
6-8 hrs |
1-2 hrs |
20-30 mins |
TYPICAL PROPERTIES UNFILLED CURED SYSTEM WITHOUT REINFORCEMENT
|
Properties |
Values |
|
Density (gm/cc) |
1.15 - 1.20
|
|
Tensile strength (kg/cm2) |
50 - 60
|
|
Compressive strength (kg/cm2) |
100 -120
|
|
Flexural strength (kg/cm2) |
120 -140
|
|
Impact strength (kg.cm/cm2) |
> 12
|
|
Water absorption (% w/w)
|
less than 0.2
|
|
Modulus of elasticity (kg/cm2) |
4000- 4500
|
|
Martens HDT (0C) |
70 - 80
|
|
Thermal conductivity (kcal /mh°C) |
0.21
|
|
Relative dielectric constant @25 °C |
4.0
|
|
Dielectric loss factor tan 8 @ 25°C |
0.003
|
|
Volume resistivity (10'5 n cm) @ 25°C |
1.2
|
|
Tracking resistance (grade) |
KA3C
|
|
Min. dielectric strength (kV/cm) |
190 -210
|
SAEFTY PRECAUTIONS:
Direct contact of Resin/Hardener with skin should be avoided. Use of hand gloves while handling them is recommended. Splashes on the skin, if any, should be removed immediately with soap and lukewarm water or with a suitable remover.
STORAGE:
Should be stored in closed containers in cool condition away from direct sunlight. Shelf life of Resin & Hardener @ 25°C is about 18 months from the date of manufacturing.
NOTE:
The information given in this literature is based on the present state of our knowledge but any conclusions and recommendations are made without any liability on our part. Buyers and users should make their own assessment of our products under their own conditions and for their own requirements.